Shall consist of No. 1 bare, uncoated, unalloyed copper wire, commonly known as Bare Bright copper wire. Wire gauge subject to agreement between buyer and seller. Green copper wire and hydraulically compacted material to be subject to agreement between buyer and seller.

توت

سیم مسی شماره 1
Shall consist of clean, untinned, uncoated, unalloyed copper wire and cable, free of brittle burnt wire. Wire gauge subject to agreement between buyer and seller. Free of copper tubing. Hydraulically briquetted copper subject to agreement.

توس

سیم مسی شماره 2
Shall consist of miscellaneous, unalloyed copper wire having a nominal 96% copper content (minimum 94%) as determined by electrolytic assay. Should be free of the following: Excessively leaded, tinned, soldered copper wire; brass and bronze wire; excessive oil content, iron, and non-metallics; copper wire from burning; insulation; hair wire; brittle burnt wire; and should be reasonably free of ash. Hydraulically briquetted copper subject to agreement.

نبات

No. 1 HEAVY COPPER SOLIDS AND TUBING
Shall consist of clean, unalloyed, uncoated copper clippings, punchings, bus bars, commutator segments, and clean copper tubing. Hydraulically briquetted copper subject to agreement.

Berry/Candy Candy/Berry

A combination of copper wire and heavy copper as defined inBerry and Candy.See above.

صخره

No. 2 COPPER SOLIDS AND TUBING
Shall consist of miscellaneous, unalloyed copper scrap having a nominal 96% copper content (minimum 94%) as determined by electrolytic assay. Should be free of the following: Excessively leaded, tinned, soldered copper scrap; brasses and bronzes; excessive oil content, iron and non-metallics; copper tubing with other than copper connections or with sediment; copper wire from burning; insulation; hair wire; brittle burnt wire; and should be reasonably free of ash. Hydraulically briquetted copper subject to agreement.

Birch/Cliff

A combination of No. 2 copper wire and copper as defined inBirch and Cliff.See above.

میخک

شماره 1 ندول های سیم مسی
Shall consist of No. 1 bare, uncoated, unalloyed copper wire scrap nodules, chopped or shredded, free of tin, lead, zinc, aluminum, iron, other metallic impurities, insulation, and other foreign contamination. Minimum copper 99%. Gauge smaller than No. 16 B & S wire and hydraulically compacted material subject to agreement between buyer and seller.

مار کبری

شماره 2 ندول های سیم مسی
Shall consist of No. 2 unalloyed copper wire scrap nodules, chopped or shredded, minimum 97% copper. Maximum metal impurities not to exceed 0.50% aluminum and 1% each of other metals or insulation. Hydraulically compacted material subject to agreement between buyer and seller.

كاكائو

COPPER WIRE NODULES
Shall consist of unalloyed copper wire scrap nodules, chopped or shredded, minimum 99% copper. Shall be free of excessive insulation and other non-metallics. Maximum metal impurities as follows: Aluminum .05% Antimony .01% Tin .25% Iron .05% Nickel .05% Hydraulically compacted material subject to agreement between buyer and seller.

خواب

LIGHT COPPER
Shall consist of miscellaneous, unalloyed copper scrap having a nominal 92% copper content (minimum 88%) as determined by electrolytic assay and shall consist of sheet copper, gutters, downspouts, kettles, boilers, and similar scrap. Should be free of the following: Burnt hair wire; copper clad; plating racks; grindings; copper wire from burning, containing insulation; radiators and fire extinguishers; refrigerator units; electrotype shells; screening; excessively leaded, tinned, soldered scrap; brasses and bronzes; excessive oil, iron and non-metallics; and should be reasonably free of ash. Hydraulically briquetted copper subject to agreement. Any items excluded in this grade are also excluded in the higher grades above.

نوشیدن

REFINERY BRASS
Shall contain a minimum of 61.3% copper and maximum 5% iron and to consist of brass and bronze solids and turnings, and alloyed and contaminated copper scrap. Shall be free of insulated wire, grindings, electrotype shells and non-metallics. Hydraulically briquetted material subject to agreement.

خوانده

ضایعات سیم مسی عایق
Shall consist of No. 2 copper wire (see Birch) with various types of insulation. To be sold on a sample or recovery basis, subject to agreement between buyer and seller. Existence of jelly wire subject to agreement between buyer and seller.

رمه

COPPER-BEARING SCRAP
Shall consist of miscellaneous copper-containing skimmings, grindings, ashes, irony brass and copper, residues and slags. Shall be free of insulated wires; copper chlorides; unprepared tangled material; large motors; pyrophoric material; asbestos brake linings; furnace bottoms; high lead materials; graphite crucibles; and noxious and explosive materials. Fine powdered material by agreement. Hydraulically briquetted material subject to agreement.

دروید

ضایعات سیم مسی عایق
Shall consist of No. 1 bare, uncoated, unalloyed copper wire (see Barley), not smaller than No. 16 B & S wire gauge (unless smaller wire gauge is mutually agreed upon), with various types of insulation. To be sold on sample or recovery basis, subject to agreement between buyer and seller.

آبنوس

ترکیب یا برنج قرمز
Shall consist of red brass scrap, valves, machinery bearings and other machinery parts, including miscellaneous castings made of copper, tin, zinc, and/or lead. Shall be free of semi-red brass castings (78% to 81% copper); railroad car boxes and other similar high-lead alloys; cocks and faucets; closed water meters; gates; pot pieces; ingots and burned brass; aluminum, silicon, and manganese bronzes; iron and non-metallics. No piece to measure more than 12” over any one part or weigh over 100 lbs. Heavier pieces acceptable upon mutual agreement between buyer and seller.

Ebulent

LEAD-FREE BISMUTH BRASS SOLIDS
Shall consist of scrap castings alloyed with copper, tin, bismuth, and zinc. Castings shall be free of leaded brass attachments and have less than 0.2% alloyed lead or as agreed between buyer and seller. Examples that meet this specification include, but are not limited to, CDA 89833/35/36/37/41/42 and 45.

عجیب و غریب

LEAD-FREE BISMUTH BRASS TURNINGS
Shall consist of scrap borings and turnings alloyed with copper, tin, bismuth, and zinc. Turnings shall be unmixed and have less than 0.2% alloyed lead or as agreed between buyer and seller. Examples that meet this specification include, but are not limited to, CDA 89833/35/36/37/41/42 and 45.

ایلند

HIGH GRADE—LOW LEAD BRONZE/BRASS SOLIDS
It is recommended these materials be sold by analysis.

ارشد

GENUINE BABBITT-LINED BRASS BUSHINGS
Shall consist of red brass bushings and bearings from automobiles and other machinery, shall contain not less than 12% high tin-base babbitt, and shall be free of iron-backed bearings.

الیاس

HIGH LEAD BRONZE SOLIDS AND BORINGS
It is recommended that these materials be sold on sample or analysis.

Enerv

RED BRASS COMPOSITION TURNINGS
Shall consist of turnings from red brass composition material and should be sold subject to sample or analysis.

فرشته

MACHINERY OR HARD BRASS SOLIDS
Shall have a copper content of not less than 75%, a tin content of not less than 6%, and a lead content of not less than 6% nor more than 11%, and total impurities, exclusive of zinc, antimony, and nickel of not more than 0.75%; the antimony content not to exceed 0.50%. Shall be free of lined and unlined standard red car boxes.

ایرلند

MACHINERY OR HARD BRASS BORINGS
Shall have a copper content of not less than 75%, a tin content of not less than 6%, and a lead content of not less than 6% nor more than 11%, and the total impurities, exclusive of zinc, antimony, and nickel of not more than 0.75%; the antimony content not to exceed 0.50%.

حصار

UNLINED STANDARD RED CAR BOXES (CLEAN JOURNALS)
Shall consist of standard unlined and/or sweated railroad boxes and unlined and/or sweated car journal bearings, free of yellow boxes and iron-backed boxes.

کشتی

LINED STANDARD RED CAR BOXES (LINED JOURNALS)
Shall consist of standard babbitt-lined railroad boxes and/or babbitt-lined car journal bearings, free of yellow boxes and iron-backed boxes.

انگور

COCKS AND FAUCETS
Shall consist of mixed clean red and yellow brass, including chrome or nickel-plated, free of gas cocks, beer faucets, and aluminum and zinc base die cast material, and to contain a minimum of 35% semired.

عسل

YELLOW BRASS SCRAP
Shall consist of mixed yellow brass solids, including brass castings, rolled brass, rod brass, tubing and miscellaneous yellow brasses, including plated brass. Must be free of manganese-bronze, aluminumbronze, unsweated radiators or radiator parts, iron, and excessively dirty and corroded materials. Must also be free of any type of munitions including, but not limited to, bullet casings.

عاج

YELLOW BRASS CASTINGS
Shall consist of yellow brass castings in crucible shape, no piece to measure more than 12 inches over any one part; and shall be free of brass forgings, silicon bronze, aluminum bronze and manganese bronze, and not to contain more than 15% nickel plated material.

برچسب

قیچی برنجی جدید
Shall consist of the cuttings of new unleaded yellow brass sheet or plate, to be clean and free from foreign substances and not to contain more than 10% of clean brass punchings under 1 /4 inch. To be free of Muntz metal and naval brass.

توری

پوسته های برنجی بدون پرایمر
Shall consist of clean fired 70/30 brass shell cases free of primers and any other foreign material. For material to be exported from the United States, all shells must be sufficiently mutilated to prevent reuse and reloading.

خانم

BRASS SHELL CASES WITH PRIMERS
Shall consist of clean fired 70/30 brass shell cases containing the brass primers, and containing no other foreign material. For material to be exported from the United States, all shells must be sufficiently mutilated to prevent reuse and reloading.

دریاچه

BRASS SMALL ARMS AND RIFLE SHELLS, CLEAN FIRED
Shall consist of clean fired 70/30 brass shells free of bullets, iron and any other foreign material. For material to be exported from the United States, all shells must be sufficiently mutilated to prevent reuse and reloading.

گوشت بره

BRASS SMALL ARMS AND RIFLE SHELLS, CLEAN MUFFLED (POPPED)
Shall consist of clean muffled (popped) 70/30 brass shells free of bullets, iron and any other foreign material. For material to be exported from the United States, all shells must be sufficiently mutilated to prevent reuse and reloading.

لارک

YELLOW BRASS PRIMER
Shall consist of clean yellow brass primers, burnt or unburnt. Shall be free of iron, excessive dirt, corrosion and any other foreign material.

ذرت

MIXED NEW NICKEL SILVER CLIPPINGS
Shall consist of one or more nickel silver alloys and the range of nickel content to be specified, free of chrome or any other plating material. Leaded nickel silver clippings should be packed and sold separately. Not to contain more than 10% of clean punchings under 1 /4 inch.

عمده

NEW NICKEL SILVER CLIPPINGS AND SOLIDS
Shall consist of new, clean nickel silver clippings, plate, rod and forgings, and other rolled shapes, free of chrome or any other plating material. Must be sold on nickel content specifications such as 10%– 12%–15%– 18%–20%. Leaded nickel silver clippings should be packed and sold separately. A description as to its physical characteristics should be made in offering all nickel silver material.

مالار

NEW SEGREGATED NICKEL SILVER CLIPPINGS
Shall consist of one specified nickel silver alloy. Not to contain more than 10% of clean punchings under 1 /4 inch.

مالیک

OLD NICKEL SILVER
Shall consist of old nickel silver sheet, pipe, rod, tubes, wire, screen, soldered or unsoldered. Must not be trimmed seams alone, and must also be free of foreign substances, iron rimmed material and other metals.

Melon BRASS PIPE Shall consist of brass pipe free of plated and soldered materials or pipes with cast brass connections. To be sound, clean pipes free of sediment and condenser tubes.

نگی

NICKEL SILVER CASTINGS
To be packed and sold separately.

دختر برادر یا خواهر و غیره

NICKEL SILVER TURNINGS
To be sold by sample or analysis.

نوظهور

LEADED BRASS SCRAP TURNINGS
Shall consist of scrap borings and turnings alloyed with copper, zinc, and lead. Turnings shall be unmixed and have less than 0.01% alloyed bismuth and silicon each and other impurities as agreed between buyer and seller.

تو رفتگی در دیوار

LEADED BRASS SCRAP ROD ENDS AND FORGINGS
Shall consist of scrap rod ends and forgings alloyed with copper, zinc, and lead. Solids shall have less than 0.01% alloyed bismuth and silicon each and other impurities as agreed between buyer and seller.

شب

YELLOW BRASS ROD TURNINGS
Shall consist strictly of rod turnings, free of aluminum, manganese, composition, Tobin and Muntz metal turnings; not to contain over 3% free iron, oil or other moisture; to be free of grindings and babbitts; to contain not more than 0.30% tin and not more than 0.15% alloyed iron.

نجیب

انتهای میله برنجی زرد جدید
Shall consist of new, clean rod ends from free turning brass rods or forging rods, not to contain more than 0.30% tin and not more than 0.15% alloyed iron. To be free of Muntz metal and naval brass or any other alloys. To be in pieces not larger than 12” and free of foreign matter.

خانه بدوش

YELLOW BRASS TURNINGS
Shall consist of yellow brass turnings, free of aluminum, manganese and composition turnings, not to contain over 3% of free iron, oil or other moisture; to be free of grindings and babbitts. To avoid dispute, to be sold subject to sample or analysis.

اقیانوس

MIXED UNSWEATED AUTO RADIATORS
Shall consist of mixed automobile radiators, to be free of aluminum radiators, and iron-finned radiators. All radiators to be subject to deduction of actual iron. The tonnage specification should cover the gross weight of the radiators, unless otherwise specified.

پالس

BRASS CONDENSER TUBES
Shall consist of clean condenser tubing which may be plated or unplated, free of excessive corroded material as mutually agreed. Upon mutual agreement between buyer and seller, may be in the form of whole bundles including iron and/or brass heads as well as iron and/or brass baffles.

پالو

لوله های کندانسور برنجی آلومینیومی
Shall consist of clean sound condenser tubing which may be plated or unplated, free of nickel alloy and corroded material.

پالم ها

MUNTZ METAL TUBES
Shall consist of clean sound Muntz metal tubing which may be plated or unplated, free of nickel alloy, aluminum alloy, and corroded material.

پارچ

MANGANESE BRONZE SOLIDS
Shall have a copper content of not less than 55%, a lead content of not more than 1%, and shall be free of aluminum bronze and silicon bronze.

آلومینیوم

قرص

CLEAN ALUMINUM LITHOGRAPHIC SHEETS
To consist of 1000 and/or 3000 series alloys, to be free of paper, plastic, excessively inked sheets, and any other contaminants. Minimum size of 3” (8 cm) in any direction.

تابلو

NEW, CLEAN ALUMINUM LITHOGRAPHIC SHEETS
To consist of 1000 and/or 3000 series alloys, uncoated, unpainted, to be free of paper, plastic, ink, and any other contaminants. Minimum size of 3” (8 cm) in any direction.

تابو

MIXED LOW COPPER ALUMINUM CLIPPINGS AND SOLIDS
Shall consist of new, clean, uncoated and unpainted low copper aluminum scrap of two or more alloys with a minimum thickness of 0.015 inches (.38 mm) and to be free of 2000 and 7000 series, hair wire, wire screen, punchings less 1/2 inch (1.25 cm) diameter, dirt, and other non-metallic items. Grease and oil not to total more than 1%. Variations to this specification should be agreed upon prior to shipment between the buyer and seller.

Taint/Tabor

CLEAN MIXED OLD ALLOY SHEET ALUMINUM
Shall consist of clean old alloy aluminum sheet of two or more alloys, free of foil, venetian blinds, castings, hair wire, screen wire, food or beverage containers, radiator shells, airplane sheet, bottle caps, plastic, dirt, and other non-metallic items. Oil and grease not to total more than 1%. Up to 10% Tale permitted.

گرفتن

NEW ALUMINUM CAN STOCK
Shall consist of new low copper aluminum can stock and clippings, clean, lithographed or not lithographed, and coated with clear lacquer but free of lids with sealers, iron, dirt and other foreign contamination. Oil not to exceed 1%.

طلق

POST-CONSUMER ALUMINUM CAN SCRAP
Shall consist of old aluminum food and/or beverage cans. The material is to be free of other scrap metals, foil, tin cans, plastic bottles, paper, glass, and other non-metallic items. Variations to this specification should be agreed upon priorto shipment between the buyer and seller.

Talcred

SHREDDED ALUMINUM USED BEVERAGE CAN (UBC) SCRAP
Shall have a density of 12 to 17 pounds per cubic foot (193 to 273 kg/m3). Material should contain maximum 5% fines less than 4 mesh (U.S. standard screen size) (6.35 mm). Must be magnetically separated material and free of steel, lead, bottle caps, plastic cans and other plastics, glass, wood, dirt, grease, trash, and other foreign substances. Any free lead is basis for rejection. Any and all aluminum items, other than used beverage cans, are not acceptable. Variations to this specification should be agreed upon prior to shipment between the seller and buyer.

Taldack

DENSIFIED ALUMINUM USED BEVERAGE CAN (UBC) SCRAP
Shall have a biscuit density of 35 to 50 pounds per cubic foot (562 to 802 kg/m3). Each biscuit not to exceed 60 pounds (27.2 kg). Nominal biscuit size range from 10” to 13” x 101/4” (25.4 x 33 x 26 cm) to 20” x 61/4” x 9” (50.8 x 15.9 x 22.9 cm). Shall have banding slots in both directions to facilitate bundle banding. All biscuits comprising a bundle must be of uniform size. Size: Bundle range dimensions acceptable are 41” to 44” x 51” (104 to 112 cm) to 54” x 54” (137 x 137 cm) to 56” (142 cm) high. The only acceptable tying method shall be as follows: Using minimum 5/8” (1.6 cm) wide by .020” (.05 cm) thick steel straps, the bundles are to be banded with one vertical band per row and a minimum of two firth (horizontal) bands per bundle. Use of skids and/or support sheets of any material is not acceptable. Must be magnetically separated material and free of steel, lead, bottle caps, plastic cans and other plastic, glass, wood, dirt, grease, trash, and other foreign substances. Any free lead is basis for rejection. Any and all aluminum items, other than used beverage cans, are not acceptable. Items not covered in the specifications, including moisture, and any variations to this specification should be agreed upon prior to shipment between the seller and buyer.

Taldon

BALED ALUMINUM USED BEVERAGE CAN (UBC) SCRAP
Shall have a minimum density of 14 pounds per cubic foot (225 kg/m3), and a maximum density of 17 pounds per cubic foot (273 kg/m3) for unflattened UBC and 22 pounds per cubic foot (353 kg/m3) for flattened UBC. Size: Minimum 30 cubic feet (.85 m3), with bale range dimensions of 24” to 40” (61 to 132 cm) by 30” to 52” (76 to 132 cm) by 40” to 84”(102 to 213 cm). The only acceptable tying method shall be as follows: four to six 5/8” (1.6 cm) x .020” (5 mm) steel bands, or six to ten #13 gauge steel wires (aluminum bands or wires are acceptable in equivalent strength and number). Use of skids and/ or support sheets of any material is not acceptable. Must be magnetically separated material and free of steel, lead, bottle caps, plastic cans and other plastic, glass, wood, dirt, grease, trash, and other foreign substances. Any free lead is basis for rejection. Any and all aluminum items, other than used beverage cans, are not acceptable. Variations to this specification should be agreed upon prior to shipment between the buyer and seller.

Taldork

BRIQUETUED ALUMINUM USED BEVERAGE CAN (UBC) SCRAP
Shall have a briquette density of 50 pounds per cubic foot (800 kg/m3) minimum. Nominal briquette size shall range from 12” to 24” (30.5 x 61 cm) x 12” to 24” (30.5 x 61 cm) in uniform profile with a variable length of 8” (20.3 cm) minimum and 48” (122 cm) maximum. Briquettes shall be bundled or stacked on skids and secured with a minimum of one vertical band per row and a minimum of one girth band per horizontal layer. Briquettes not to overhang pallet. Total package height shall be 48 (122 cm) maximum. Banding shall be at least 5/8” (1.6 cm) wide by .020” (5 mm) thick steel strapping or equivalent strength. The weight of any bundle shall not exceed 4,000 pounds (1.814 mt). Material must be magnetically separated and free of steel, plastic, glass, dirt and all other foreign substances. Any and all aluminum items other than UBC are unacceptable. Any free lead is basis for rejection. Items not covered in the specification, including moisture, and any variations to this specification should be agreed upon prior to shipment between the buyer and seller.

داستان

PAINTED SIDING
Shall consist of clean, low copper aluminum siding scrap, painted one or two sides, free of plastic coating, iron, dirt, corrosion, fiber, foam, or fiberglass backing or other non-metallic items.

صحبت

ALUMINUM COPPER RADIATORS
Shall consist of clean aluminum and copper radiators, and/or aluminum fins on copper tubing, free of brass tubing, iron and other foreign contamination.

بلند قد

E.C. ALUMINUM CHOPS AND STRAWS
Shall consist of clean, 1350 and/or 1050 alloy, E.C. aluminum, chops or straws, free of screening, hairwire, iron, copper, insulation and other non-metallic items. Must be free of minus 20 mesh material. Must contain 99.45% aluminum content.

تالی

ALL ALUMINUM RADIATORS FROM AUTOMOBILES
Shall consist of clean aluminum radiators and/or condensers. Should be free of all other types of radiators. All contaminants including iron, plastic, and foam not to exceed 1% of weight. Any deviation to this specification, including oxidation and aluminum content, to be negotiated between buyer and seller.

طلون

E.C. ALUMINUM WIRE and CABLE
Shall consist of new, clean, 1350 and/or 1050, E.C. aluminum wire or cable free from hair wire, ACSR, wire screen, tape, iron, insulation and other non-metallic items. Must contain 99.45% aluminum content.

مخزن

ALUMINUM CHOPS and STRAWS
Shall consist of clean aluminum, chops or straws, free of screening, hair-wire, iron, copper, insulation and other non-metallic items. Must be free of minus 20 mesh material. Must contain 99% aluminum content.

صنوبر

NEW MIXED ALUMINUM WIRE AND CABLE
Shall consist of new, clean, unalloyed aluminum wire or cable which may contain up to 10% 6000 series wire and cable free from hair wire, wire screen, iron, insulation and other non-metallic items.

Tarry A

CLEAN ALUMINUM PISTONS
Shall consist of clean aluminum pistons to be free from struts, bushings, shafts, iron rings and nonmetallic items. Oil and grease not to exceed 2%.

Tarry B

CLEAN ALUMINUM PISTONS WITH STRUTS
Shall consist of clean whole aluminum pistons with struts. Material is to be free from bushings, shafts, iron and non-metallic items . Oil and grease not to exceed 2%.

Tarry C

IRONY ALUMINUM PISTONS
Shall consist of aluminum pistons with non-aluminum attachments to be sold on a recovery basis or by special arrangement between buyer and seller.

تسلس

OLD MIXED ALUMINUM WIRE AND CABLE
Shall consist of old, unalloyed aluminum wire and cable which may contain up to 10% 6000 series wire and cable with not over 1% free oxide or dirt and free from hair wire, wire screen, iron, insulation and other non-metallic items.

طعم

OLD PURE ALUMINUM WIRE AND CABLE
Shall consist of old, unalloyed aluminum wire and cable containing not over 1% free oxide or dirt and free from hair wire, wire screen, iron, insulation and other non-metallic items.

تاتا

NEW PRODUCTION ALUMINUM EXTRUSIONS
Shall consist of one alloy (typically 6063). Material may contain “butt ends” from the extrusion process but must be free of any foreign contamination. Anodized material is acceptable. Painted material or alloys other than 6063 must be agreed upon by buyer and seller.

بهبرای

ALUMINUM EXTRUSIONS
“10/10” Material to consist of new production and old/used 6063 extrusions that may contain up to (but not exceed) 10 percent painted extrusions and 10 percent 6061 alloy extrusions. Must not contain other alloys of aluminum. Material should be free of zinc corners, iron attachments, felt, plastic, paper, cardboard, thermo break, and dirt and other contaminants.

توتو

ALUMINUM EXTRUSION DEALER GRADE
Shall consist of old extruded aluminum of one alloy, typically alloy 6063, 6061, or 7075. Material must be free of iron, thermo break, saw chips, zinc corners, dirt, paper, cardboard, and other foreign contamination. Percentages of paint or other alloys to be agreed upon by buyer and seller.

کسی را دست انداختن

ALUMINUM WIRE and CABLE

Shall consist of new, clean, aluminum wire or cable free from hair wire, ACSR, wire screen, iron, insulation and other nonmetallic items. Must contain 99% aluminum content.

TURNINGS
Shall consist of aluminum borings and turnings of one specified alloy. Material should be free of oxida- tion, dirt, free iron, stainless steel, magnesium, oil, flammable liquids, moisture and other non-metallic items. Fines should not exceed 3% through a 20 mesh (U.S. standard) screen.

Telic

MIXED ALUMINUM BORINGS AND TURNINGS
Shall consist of clean, uncorroded aluminum borings and turnings of two or more alloys and subject to deductions for fines in excess of 3% through a 20 mesh screen and dirt, free iron, oil, moisture and all other nonmetallic items. Material containing iron in excess of 10% and/or free magnesium or stainless steel or containing highly flammable cutting com- pounds will not constitute good delivery. To avoid dispute, material should be sold on basis of definite maximum zinc, tin and magnesium content.

سفت

MIXED ALUMINUM CASTINGS
Shall consist of all clean aluminum castings which may contain auto and airplane castings but no ingots, and to be free of iron, brass, dirt and other non-metallic items. Oil and grease not to total more than 2%.

تپید

AIRCRAFT SHEET ALUMINUM
Should be sold on recovery basis or by special arrangements with purchaser.

ترس

NEW ALUMINUM FOIL
Shall consist of clean, new, pure, uncoated 1000 and/or 3000 and/or 8000 series alloy aluminum foil, free from anodized foil, radar foil and chaff, paper, plastics, or any other non-metallic items. Hydraulically briquetted material and other alloys by agreement between buyer and seller.

تسلا

POST CONSUMER ALUMINUM FOIL
Shall consist of baled old household aluminum foil and formed foil containers of uncoated 1000, 3000 and 8000 series aluminum alloy. Material may be anodized and contain a maximum of 5% organic residue. Material must be free from radar chaff foil, chemically etched foil, laminated foils, iron, paper, plastic and other non-metallic contaminants.

تترا

NEW COATED ALUMINUM FOIL
Shall consist of new aluminum foil coated or laminated with ink, lacquers, paper, or plastic. Material shall be clean, dry, free of loose plastic, PVC and other non-metallic items. This foil is sold on a metal content basis or by sample as agreed between buyer and seller.

ران

ALUMINUM GRINDINGS
Should be sold on recovery basis or by special arrangements with purchaser.

Thirl

ALUMINUM DROSSES, SPATTERS, SPILLINGS, SKIMMINGS AND SWEEPINGS
Should be sold on recovery basis or by special arrangements with purchaser.

خار

ALUMINUM BREAKAGE
Shall consist of aluminum with miscellaneous contaminants like iron, dirt, plastic and other types of contaminants. Material can either be sold based on aluminum recovery or content as agreed upon by buyer and seller. Must contain a minimum of 33% aluminum unless otherwise agreed upon by buyer and seller.

ضربان

SWEATED ALUMINUM
Shall consist of aluminum scrap which has been sweated or melted into a form or shape such as an ingot, sow or slab for convenience in shipping; to be free from corrosion, dross or any non-aluminum inclusions. Should be sold subject to sample or analysis.

دندان

SEGREGATED NEW ALUMINUM ALLOY CLIPPINGS AND SOLIDS
Shall consist of new, clean, uncoated and unpainted aluminum scrap of one specified aluminum alloy with a minimum thickness of .015” (.38 mm) and to be free of hair wire, wire screen, dirt and other nonmetallic items. Oil and grease not to total more than 1%. Also free from punchings less than 1/2” (1.27 cm) in size.

سخت است

MIXED NEW ALUMINUM ALLOY CLIPPINGS AND SOLIDS
Shall consist of new, clean, uncoated and unpainted aluminum scrap of two or more alloys with a minimum thickness of .015” (.38 mm) and to be free of hair wire, wire screen, dirt and other non-metallic items. Oil and grease not to total more than 1%. Also free from punchings less than 1/2” (1.27 cm) in size.

راه رفتن

SEGREGATED NEW ALUMINUM CASTINGS, FORGINGS AND EXTRUSIONS
Shall consist of new, clean, uncoated aluminum castings, forgings, and extrusions of one specified alloy only and to be free from sawings, stainless steel, zinc, iron, dirt, oil, grease and other non-metallic items. Troma Aluminum Auto or Truck Wheels Shall consist of clean, single-piece, unplated aluminum wheels of a single specified alloy, free of all inserts, steel, wheel weights, valve stems, tires, grease and oil and other non-metallic items. Variations to this specification should be agreed upon prior to shipment between the buyer and seller.

مغلوب ساختن پیشی جستن

ALUMINUM AUTO CASTINGS
Shall consist of all clean automobile aluminum castings of sufficient size to be readily identified and to be free from iron, dirt, brass, bushings, and non-metallic items. Oil and grease not to total more than 2%.

تریل

ACSR
Aluminum Conductor Steel Reinforced (ACSR) wire is a combination of steel and aluminum wire, of various configurations, with the expected aluminum recovery agreed upon by the buyer and the seller. Material to be free of other wires and cables unless mutually agreed upon. Twang IAW Insulated aluminum wire, which may or may not contain other wires or metal shielding, with the expected aluminum recovery agreed upon by the buyer and the seller. The material to be free of other wires and cables unless mutually agreed upon.

چرخش

FRAGMENTIZER AIRCRAFT ALUMINUM SCRAP
(2000 and 7000 series) The material as received must be dry and not to contain more than 2% free zinc, 1% maximum free magnesium, and 1.5% maximum free iron and stainless with a maximum of 2% analytical iron. Not to contain more than a total 5% maximum of non-metallics, of which no more than 1% shall be rubber and plastics. To be free of excessively oxidized material. Any variations to be sold by special arrangement between buyer and seller.

پیچ

ALUMINUM AIRPLANE CASTINGS
Shall consist of clean aluminum castings from airplanes and to be free from iron, dirt, brass, bushings, and non-metallic items. Oil and grease not to total more than 2%.

انقباض

FLOATED FRAGMENTIZER ALUMINUM SCRAP
(from Automobile Shredders) Derived from wet or dry media separation device, the material must be dry and not contain more than 1% maximum free zinc, 1% maximum free magnesium, and 1% maximum of analytical iron. Not to contain more than a total 2% maximum of non-metallics, of which no more than 1% shall be rubber and plastics. To be free of excessively oxidized material, air bag canisters, or any sealed or pressurized items. Any variation to be sold by special arrangement between buyer and seller.

نیشگون گرفتن و کشیدن
FRAGMENTIZER ALUMINUM SCRAP
(from Automobile Shredders) Derived from either mechanical or hand separation, the material must be dry and not contain more than 4% maximum free zinc, 1% maximum free magnesium, and 1.5% maximum of analytical iron. Not to contain more than a total 5% maximum of nonmetallics, of which no more than 1% shall be rubber and plastics. To be free of excessively oxidized material, air bag canisters, or any sealed or pressurized items. Any variation to be sold by special arrangement between buyer and seller.

Twire

BURNT FRAGMENTIZER ALUMINUM SCRAP
(from Automobile Shredders) Incinerated or burned material must be dry and not contain more than X% (% to be agreed upon by buyer and seller) ash from incineration, 4% maximum free zinc, 1% maximum free magnesium, and 1.5% maximum of analytical iron. Not to contain more than a total 5% maximum of non-metallics, of which no more than 1% shall be rubber and plastics. To be free of excessively oxidized material, air bag canisters, or any sealed pressurized items. Any variation to be sold by special arrangement between buyer and seller.

قلدر

SHREDDED NONFERROUS SCRAP
(predominantly aluminum) Shall be made up of a combination of the nonferrous metals: aluminum, copper, lead, magnesium, stainless steel, nickel, tin, and zinc, in elemental or alloyed (solid) form. The percentage of each metal within the nonferrous concentrate shall be subject to agreement between buyer and seller. Material generated by eddy current, air separation, flotation, screening, other segregation technique(s), or a combination thereof. Shall have passed one or more magnets to reduce or eliminate free iron and/or large iron attachments. Shall be free of radioactive material, dross, or ash. Material to be bought/sold under this guideline shall be identified as “Zorba” with a number to follow indicating the estimated percentage nonferrous metal content of the material (e.g., “Zorba 90” means the material contains approximately 90% nonferrous metal content). May also be screened to permit description by specific size ranges. (Refer also to Zorba under Mixed Metals.)

ZINC

موجب صرفه جویی در

OLD ZINC DIE CAST SCRAP
Shall consist of miscellaneous old zinc base die castings, with or without iron and other foreign attachments. Must be free of borings, turnings, dross pieces, chunks, melted pieces and skimmings. All unmeltables, dirt, foreign attachments, and volatile substances (such as rubber, cork, plastic, grease, etc.) are deductible. Material containing in excess of 30% iron will not constitute good delivery.

گال

NEW ZINC DIE CAST SCRAP
Shall consist of new or unused, clean, zinc base die castings. Castings to be unplated, unpainted, and free from corrosion.

اسکوت

ZINC DIE CAST AUTOMOTIVE GRILLES
Shall consist of clean, old or used zinc base die cast automotive grilles, free from soldered material. All foreign attachments and extraneous materials are deductible.

حوزه

NEW PLATED ZINC DIE CAST SCRAP
Shall consist of new or unused clean, plated zinc base die castings, free from corrosion.

نمره

OLD SCRAP ZINC
Shall consist of clean dry scrap zinc, such as sheets, jar lids, clean unalloyed castings and anti-corrosion plates. Borings and turnings are not acceptable. Material must not be excessively corroded or oxidized. All foreign attachments and extraneous materials are deductible.

پرده

NEW ZINC CLIPPINGS
Shall consist of any new pure zinc sheets or stampings free from corrosion. To contain no foreign material or attachments. Printers zinc, such as engravers zinc, lithograph sheets and addressograph plates subject to special arrangements. Printers zinc to be free of routings.

کاتب نسخه های خطی

CRUSHED CLEAN SORTED FRAGMENTIZERS DIE CAST SCRAP, AS PRODUCED FROM AUTOMOBILE FRAGMENTIZERS
To be clean, free of dirt, oil, glass, rubber, and trash. To contain a maximum of 5% unmeltables such as free iron, copper, aluminum and other metals.

طومار

UNSORTED ZINC DIE CAST SCRAP
Produced from automobile fragmentizers. Material to contain about 55% zinc-bearing scrap. Other nonferrous metals such as aluminum, stainless steel, red metal, etc., to be about 40%. Insulated copper wire about 1%. Trash, dirt, glass, rubber, oil, iron, not to exceed 5%. Any variations to be sold by special arrangement between buyer and seller.

مالش دادن

HOT DIP GALVANIZERS SLAB ZINC DROSS
(Batch Process) Shall consist only of galvanizers unsweated zinc dross in slab form from hot dip galvanizing (Batch Process) with a minimum zinc content of 92% and shall be free of skimmings and tramp iron. Broken pieces under 2” in diameter shall not exceed 10% of the weight of each shipment. Slabs shall not weigh over 100 pounds each. Heavier pieces acceptable upon mutual agreement between buyer and seller. Material from continuous galvanizing operation is not acceptable. Blocks are acceptable upon mutual agreement.

جمجمه

ZINC DIE CAST SLABS OR PIGS
Shall consist of melted zinc base die cast materials, in smooth clean solid slabs or pigs. Material to be free from drosses and to contain a minimum zinc content of 90%. To contain a maximum of 0.1% nickel and maximum of 1% lead. Blocks are acceptable upon mutual agreement.

مهر

CONTINUOUS LINE GALVANIZING SLAB ZINC TOP DROSS
Shall consist of unsweated zinc dross removed from the top of a continuous line galvanizing bath, in slab form not weighing in excess of 100 pounds each, with a minimum zinc content of 90%. Heavier pieces acceptable upon mutual agreement between buyer and seller. Shall be free of skimmings. Broken pieces under 2” in diameter shall not exceed 10% of the weight of each shipment.

درز

CONTINUOUS LINE GALVANIZING SLAB ZINC BOTTOM DROSS
Shall consist of unsweated zinc dross removed from the bottom of a continuous line galvanizing bath, in slab form not weighing in excess of 100 pounds each, with a minimum zinc content of 92%. Heavier pieces acceptable upon mutual agreement between buyerand seller. Shall be free of skimmings. Broken pieces under 2” in diameter shall not exceed 10% of the weight of each shipment.

تاقچه

PRIME ZINC DIE CAST DROSS
Shall consist of metal skimmed from the top of pot of molten zinc die cast metal. Must be unsweated, unfluxed, shiny, smooth, metallic and free from corrosion or oxidation. Should be poured in molds or in small mounds weighing not over 75 pounds each.

منیزیم

ویفر

MAGNESIUM CLIPS
Shall consist of clean magnesium clips in crucible size, free of copper, aluminum, and zinc flashings and excessive oil and grease. To be free of all foreign attachments.

گردو

MAGNESIUM SCRAP
Shall consist of magnesium castings, magnesium engine blocks and transmission casings, bomber and car wheels, extrusions, and sheet. Material to be free from brass and copper inserts and all foreign attachments. To be free of anodes, hollow castings and explosives. Percentages of and penalties for dirt, oil, grease, and iron to be subject to agreement between buyer and seller. Excessively large pieces to be negotiated between buyer and seller.

شراب

MAGNESIUM ENGRAVER PLATES
To be free of copper, aluminum, zinc, and electrotype plates. To be clean and free of all foreign attachments. Magnesium plates shipped loose by agreement between buyer and seller.

چوب

MAGNESIUM DOCKBOARDS
Shall consist of clean magnesium dockboard cut or broken to size agreed upon by buyer and seller. To be free of all foreign attachments.

جهان

MAGNESIUM TURNINGS
It is recommended that these materials be sold by special arrangement between buyer and seller.

رهبری

قفسه

SCRAP LEAD—SOFT
Shall consist of clean soft scrap lead, free of other materials such as drosses, battery plates, lead covered cable, hard lead, collapsible tubes, foil, type metals, aluminum, zinc, iron and brass fittings, dirty chemical lead and radioactive materials. Review packaging specifications and regulatory status pertaining to shipping with buyer prior to sale.

رادیو

MIXED HARD/SOFT SCRAP LEAD
Shall consist of clean lead solids and lead shots, free of other materials, such as drosses, battery plates, lead covered cable, collapsible tubes, type metals, aluminum, zinc, iron and brass fittings, dirty chemical lead and radioactive materials. Review packaging specifications and regulatory status pertaining to shipping with buyer prior to sale.

باران

SCRAP DRAINED/DRY WHOLE INTACT LEAD
To be free of any liquid. Cases to be either plastic or rubber and be complete including caps. Non-lead (nicad, ni-fe, carbonaire, etc.) not acceptable. Industrial, steel cased, aircraft (aluminum cased) and partial, cracked or broken batteries and batteries without caps subject to special agreement. Review packaging specifications and regulatory status pertaining to shipping with buyer prior to sale.

رودخانه

BATTERY LUGS
To be free of scrap lead, wheel weights, battery plates, rubber and/or plastic case material and other foreign material. A minimum of 97% metallic content is required. Review packaging specifications and regulatory status pertaining to shipping with buyer prior to sale.

قرقره

MIXED NONFERROUS WHEEL WEIGHTS
To consist of nonferrous wheel weights that are a minimum of 35% (overall) Nonferrous and no more than 65% Iron (Fe). Anticipated Nonferrous material may be both Lead and Zinc weights. To be free of foreign material. Final material specifications to be determined between buyer and seller.

رله

LEAD COVERED COPPER CABLE
Free of armored covered cable and foreign material subject to negotiation between buyer and seller.

اجاره

LEAD DROSS
Should be clean and reasonably free of other materials such as iron, dirt, harmful chemicals or other metals. To be free of radioactive materials, aluminum and zinc. May be bought on an assay basis or as agreed to by buyer and seller. Other metals present such as antimony, tin, etc., to be accounted for as agreed between buyer and seller. Material to be readily dumped from drums. An extra charge may be assessed if material has to be mechanically removed. Review packaging specification and regulatory status pertaining to shipping with buyer prior to sale.

غرق

SCRAP WET WHOLE INTACT LEAD BATTERIES
Consisting of SLI (starting, lighting & ignition), automotive, truck, 8-D and commercial golf cart and marine-type batteries. Cases to be either plastic or rubber and to be complete. Non-lead (i.e., ni-cad, ni-fe, carbonaire, etc.) not acceptable. Other types i.e. aircraft (aluminum) gel-cel, lawnmower, etc., and partial, cracked or broken batteries or batteries without caps and the amount of liquid content and any variations to the specification subject to special agreement. Review packaging specifications and regulatory status pertaining to shipping with buyer prior to sale.

رونو

SCRAP INDUSTRIAL INTACT LEAD CELLS
Consisting of plates enclosed by some form of complete plastic case. Partial, cracked or broken cells, cells without caps and the amount of liquid content and any variations to the specification subject to special agreement. Review packaging specifications and regulatory status pertaining to shipping with buyer prior to sale.

روپر

SCRAP WHOLE INTACT INDUSTRIAL LEAD BATTERIES
Consisting of bus, diesel, locomotive, telephone and/ or steel cased batteries. Submarine batteries subject to negotiation. Partial, cracked, broken batteries or batteries without caps and the amount of liquid content and any variations to the specification subject to special agreement. Review packaging specifications and regulatory status pertaining to shipping with buyer prior to sale.

طناب

LEAD WHEEL WEIGHTS
To consist of lead wheel weights with or without iron clips. Not to include scrap lead, lugs or plates unless specifically agreed to. To be free of foreign material. Final material specifications to be determined between buyer and seller.

NICKEL/STAINLESS/HI TEMP

عطر

NEW NICKEL SCRAP
Shall consist of clean new sheet, plate, bar, tube, and any other wrought nickel scrap solids. Nickel minimum 99%; Cobalt maximum 0.25%; Copper maximum 0.50%. Free of castings, as well as any foreign attachments or other contamination.

تنومند

OLD NICKEL SCRAP
Shall consist of old and/or newsheet, plate, bar, tube, and any other wrought nickel scrap solids. Material to contain a minimum of 98% nickel; Copper maximum 0.50%. This grade to be free of castings, soldered, brazed, sweated, or painted material, other metallic coating, foreign attachments, or any other contamination.

شیک پوش

NEW CUPRO NICKEL CLIPS AND SOLIDS
Shall consist of clean, new, segregated (normally accepted analysis grades) either 70/30, 80/20, or 90/10 cupro nickel tube, pipe, sheet, plate, or other wrought solid forms. Must be free of foreign attachments or any other contamination.

دلهره آور

CUPRO NICKEL SOLIDS
Shall consist of old, and/or new, segregated (normally accepted analysis grades) either 70/30, 80/20, 90/10 cupro nickel tube, pipe, sheet, plate, or other wrought solid forms. Maximum 2% sediment allowable. Any other forms of cupro nickel solids such as castings, gates, risers, spills, etc., packaged separately, may or may not be included, only upon agreement between buyer and seller. Must be free of foreign attachments and all other contamination. Other particulars concerning physical description, analysis and packaging to be agreed upon between buyer and seller.

دام

CURPO NICKEL SPINNINGS, TURNINGS, BORINGS
Shall consist of clean, segregated (normally accepted analysis grades) either 70/30, 80/20, 90/10 cupro nickel spinnings, turnings, or borings. Particulars concerning physical description, analysis, and packaging, to be agreed upon between buyer and seller.

دلتا

SOLDERED CUPRO NICKEL SOLIDS
Shall consist of segregated (normally accepted analysis grades) either 70/30, 80/20, 90/10 cupro nickel solids, soldered, brazed, or sweated material. Must be free of trimmed seams and edges and all other contamination.

عمق

MISCELLANEOUS NICKEL-COPPER AND NICKEL-COPPER IRON
Shall consist of miscellaneous scrap in which the basic elements, by weight, are nickel and copper, such as copper nickel peelings, plating racks, and hangers, and all nickel and copper in attached or combined form. In all cases, miscellaneous nickel copper scrap should be sold by description and analysis.

تکان دادن

NEW R-MONEL CLIPPINGS AND SOLIDS
Shall consist of clean, new, R-Monel sheet, plate, bar, rod, tube, pipe, or any other wrought scrap. Must be free of any foreign attachments or all other contamination.

خانه

NEW MIXED MONEL SOLIDS AND CLIPPINGS
Shall consist of new, clean R and K-Monel solids and clippings. Free of cast material, foreign attachments and all other contamination.

ایده آل

OLD MONEL SHEET AND SOLIDS
Shall consist of clean R and K-Monel solids such as sheet, plate, pipe, rods, forgings, screen and wire cloth. Must be free of soldered, brazed, welded, or sweated material, cast material, foreign attachments, and all other contamination.

هندی

K-MONEL SOLIDS
Shall consist of clean K-Monel solids.

با هم

SOLDERED MONEL SHEET AND SOLIDS
Shall consist of soldered and/or brazed miscellaneous grades of Monel alloys in either wrought or cast form. Must be free of trimmed seams and edges, non-metallic filling, foreign attachments, and all other contamination. Particulars concerning physical description, assay, and packaging to be agreed upon between buyer and seller.

لیمو

MONEL CASTINGS
Shall consist of various types of clean Monel castings, assaying minimum 60% nickel. Must be free of foreign attachments or any other contamination.

لمور

MONEL TURNINGS
Shall consist of mixed Monel turnings and borings containing a minimum of 60% nickel content, on a dry basis.

پکو

200 SERIES STAINLESS STEEL SCRAP SOLIDS
Shall consist of all types of cleanAISISeriesStainless SteelScrapSolids, which contain a maximum of .5% copper, free of foreign attachments and other contamination.

کفش چوبی روستاییان اروپا

STAINLESS STEEL SCRAP
Shall consist of clean 18-8 type stainless steel clips and solids containing a minimum 7% nickel, 16% chrome, and have a maximum of .50% molybdenum, .50% copper, .045% phosphorous, and .03% sulfur, and otherwise free of harmful contaminants. Particulars concerning physical description, grading, additional analysis, and preparation to be agreed upon between buyer and seller.

سنت

NICKEL BEARING SCRAP
Any nickel bearing alloy scrap that contains a minimum of 3% recovered nickel. Nickel content to be determined by recovery after buyer’s evaluation minus any non-conforming material and/or contamination. Balance of elements contained to be discussed between buyer and seller. Material is to be free of any foreign material. Final material specifications to be determined between buyer and seller.

افراطی

STAINLESS STEEL TURNINGS
Shall consist of clean 18-8 type stainless steel turnings containing a minimum 7% nickel and 16% chrome, and to be free of nonferrous metals, nonmetallics, excessive iron, oil and other contaminants. Particulars concerning physical description, assay, and packaging to be agreed upon between buyer and seller.

تعطیلات

EDISON BATTERIES
Nickel-iron batteries to be sold free of crates, copper terminal connectors, and excess liquid. Must be free of nickel cadmium batteries.

Zurik

SHREDDED NONFERROUS SENSOR SORTED SCRAP
(predominantly stainless steel) Shall be made up of a combination of the nonferrous metals: stainless steel, insulated copper wire, aluminum, copper, lead, magnesium, nickel, tin, and zinc, in elemental or alloyed (solid) form. The percentage of each metal within the nonferrous concentrate shall be subject to agreement between buyer and seller. Material generated by computer sensing equipment (e.g., induction sensor sorting or X-ray) technique(s). Shall have passed one or more magnets to reduce or eliminate free iron and/or large iron attachments. Shall be free of radioactive material, dross, or ash. Material to be bought/sold under this guideline shall be identified as “Zurik” with a number to follow indicating the estimated percentage nonferrous content of the material (e.g., “Zurik 90” means the material contains approximately 90% nonferrous metal content). May also be screened to permit description by specific size ranges. (Refer also to Zurik under Mixed Metals.)

MIXED METALS

دارت

BALLASTS (FLUORESCENT)
Shall consist of whole and complete fluorescent light ballasts containing copper inside. Must not contain polychlorinated biphenyls (PCBs). Electronic ballasts subject to agreement between buyer and seller.

Vader با

SEALED UNITS
Shall consist of whole steel-cased compressors originating from condensers from air conditioner units, freezers, refrigerators or the like, containing a motor inside. Free of hazardous materials, including chlorofluorocarbons (CFCs) or other refrigerants and polychlorinated biphenyls (PCBs). No loose iron or extra iron attachments such as framework permitted.

علم

MIXED ELECTRIC MOTORS
Shall consist of whole electric motors and/or dismantled electric motor parts that are primarily copperwound. May contain some aluminum-wound material, subject to agreement between buyer and seller. No excessive steel attachments such as gear reducers, iron bases, and pumps, or loose free iron allowed. Specification not to include sealed units or cast iron compressors.

Small Elmo

موتورهای الکتریکی
Shall be sized to approximately basketball size or smaller and shall consist of whole electric motors and/or dismantled electric motor parts that are primarily copper-wound. May contain some aluminumwound material, subject to agreement between buyer and seller. No excessive steel attachments such as gear reducers, iron bases, and pumps, or loose free iron allowed. Specification not to include sealed units or cast iron compressors.

انقباض

SHREDDED ELECTRIC MOTORS (also called “shredder pickings” or “meatballs”)
Shall consist of mixed copper and aluminum bearing material from ferrous shredding, comprised of motors without cases. May contain insulated copper harness wire, subject to agreement between buyer and seller. Trace percentages of other contaminants and fines may be present. No free iron or sealed units.

Shelmo

SHREDDED ELECTRIC MOTORS (also called “shredder pickings” or “meatballs”)
Shall consist of mixed copper-bearing material from ferrous shredding, comprised of motors without cases. May contain up to 5 percent aluminum-wound material and may contain insulated copper harness wire, subject to agreement between buyer and seller. Trace percentages of other contaminants and fines may be present. No free iron or sealed units.

گورخر

(High Density)
Shall consist of high-density nonferrous metals produced by media separation technology containing brass, copper, zinc, nonmagnetic stainless steel, and copper wire. Material to be dry and free from excess oxidation. The percentage and types of metals other than these, as well as the percentage and types of nonmetallic contamination, are to be agreed upon between the buyer and seller. Zeppelin(Light Density) Shall consist of light-density nonferrous metals produced by media separation technology and contain thin-gauge aluminum and magnesium. Material to be dry and free from excess oxidation. The percentage and types of metals other than aluminum and magnesium, as well as the percentage and types of nonmetallic contamination, are to be agreed upon between the buyer and seller.

Zeyda

SHREDDED INSULATED COPPER WIRE
Shall consist predominantly of recovered ICW (Insulated Copper Wire) that has been derived by either mechanical or physical separation. This material is likely to have other metals, in small percentages (should be less than 5%) that were not successfully separated. The percentage of each metal within the overall product shall be subject to agreement between buyer and seller. Shall have passed one or more magnets to reduce or eliminate free iron and/ or large iron attachments. Shall be free of radioactive material, dross, or ash. Material to be bought/ sold under this guideline shall be identified as “Zeyda” with two numbers to follow, indicating the estimated percentage recoverable copper wire and the second indicating the maximum amount of other metals or contaminants expected. (e.g., “Zeyda 45/3” means the material contains approximately 45% copper and up to 3% other material). May also be screened to permit description by specific size ranges. Zorba SHREDDED NONFERROUS SCRAP (predominantly aluminum) Shall be made up of a combination of the nonferrous metals: aluminum, copper, lead, magnesium, stainless steel, nickel, tin, and zinc, in elemental or alloyed (solid) form. The percentage of each metal within the nonferrous concentrate shall be subject to agreement between buyer and seller. Material generated by eddy current, air separation, flotation, screening, other segregation technique(s), or a combination thereof. Shall have passed one or more magnets to reduce or eliminate free iron and/or large iron attachments. Shall be free of radioactive material, dross, or ash. Material to be bought/sold under this guideline shall be identified as “Zorba” with a number to follow indicating the estimated percentage nonferrous metal content of the material (e.g., “Zorba 90” means the material contains approximately 90% nonferrous metal content). May also be screened to permit description by specific size ranges. (Refer also to Zorba under Aluminum.)

Zurik
SHREDDED NONFERROUS SENSOR SORTED SCRAP
(predominantly stainless steel) Shall be made up of a combination of the nonferrous metals: stainless steel, insulated copper wire, aluminum, copper, lead, magnesium, nickel, tin, and zinc, in elemental or alloyed (solid) form. The percentage of each metal within the nonferrous concentrate shall be subject to agreement between buyer and seller. Material generated by computer sensing equipment (e.g., induction sensor sorting or X-ray) technique(s). Shall have passed one or more magnets to reduce or eliminate free iron and/or large iron attachments. Shall be free of radioactive material, dross, or ash. Material to be bought/sold under this guideline shall be identified as “Zurik” with a number to follow indicating the estimated percentage nonferrous content of the material (e.g., “Zurik 90” means the material contains approximately 90% nonferrous metal content). May also be screened to permit description by specific size ranges. (Refer also to Zurik under Nickel/Stainless/ Hi Temp.)

OTHER

در مرتع پرورش احشام کردن

BLOCK TIN
Block tin must assay minimum of 98% tin, and to be free of liquids, solder, and brass connections, pewter, pumps, pot pieces, and dirt.

صفات

پیوتر
Shall consist of tableware and soda-fountain boxes but should contain a minimum of 84% tin. Siphon tops to be accounted for separately. Material must be free of brass, zinc, and other foreign metals.

راوها

HIGH TIN BASE BABBITT
Shall contain a minimum of 78% tin and be free of brassy or zincy metals.

گل رز

MIXED COMMON BABBITT
Shall consist of lead base bearing metal containing not less than 8% tin, free from Allens metal, ornamental, antimonial and type metal. Must be free from all zinc and excessive copper in the alloy.

فلزات آهنی

200 No. 1 heavy melting steel. Wrought iron and/or steel scrap 1/4 inch and over in thickness. Individual pieces not over 60 x 24 inches (charging box size) prepared in a manner to insure compact charging.

201 No. 1 heavy melting steel 3 feet x 18 inches. Wrought iron and/or steel scrap 1/4 inch and over in thickness. Individual pieces not over 36 x 18 inches (charging box size) prepared in a manner to insure compact charging.

202 No. 1 heavy melting steel 5 feet x 18 inches. Wrought iron and/or steel scrap 1/4 inch and over in thickness. Individual pieces not over 60 x 18 inches (charging box size) prepared in a manner to insure compact charging.

203 No. 2 heavy melting steel.* Wrought iron and steel scrap, black and galvanized, 1/8 inch and over in thickness, charging box size to include material not suitable as No. 1 heavy melting steel. Prepared in a manner to insure compact charging.

204 No. 2 heavy melting steel.* Wrought iron and steel scrap, black and galvanized, maximum size 36 x 18 inches. May include all automobile scrap properly prepared.

205 No. 2 heavy melting steel 3 feet x 18 inches. Wrought iron and steel scrap, black and galvanized, maximum size 36 x 18 inches. May include automobile scrap, properly prepared; however, to be free of sheet iron or thin gauged material.

206 No. 2 heavy melting steel 5 feet x 18 inches. Wrought iron and steel scrap, black and galvanized, maximum size 60 x 18 inches. May include automobile scrap, properly prepared; however, to be free of sheet iron or thin gauged material.

207 No. 1 busheling. Clean steel scrap, maximum size 2 feet by 5 feet, including new factory busheling (for example, sheet clippings, stampings, etc.). May not include old auto body and fender stock. Free of metal coated, limed, vitreous enameled, and electrical sheet containing over 0.5 percent silicon.

207A New black sheet clippings. For direct charging, maximum size 8 feet by 18 inches, free of old automobile body and fender stock, metal coated, lined, vitreous enameled and electrical sheet containing over 0.5 percent silicon. Must lay reasonably flat in car.

208 No. 1 bundles. New black steel sheet scrap, clippings or skeleton scrap, compressed or hand bundled, to charging box size, and weighing not less than 75 pounds per cubic foot. (Hand bundles are tightly secured for handling with a magnet.) May include Stanley balls or mandrel wound bundles or skeleton reels, tightly secured. May include chemically detinned material. May not include old auto body or fender stock. Free of metal coated, limed, vitreous enameled, and electrical sheet containing over 0.5 percent silicon.

209 No. 2 bundles. Old black and galvanized steel sheet scrap, hydraulically compressed to charging box size and weighing not less than 75 pounds per cubic foot. May not include tin or lead-coated material or vitreous enameled material.

210 Shredded scrap. Homogeneous iron and steel scrap, magnetically separated, originating from automobiles, unprepared No. 1 and No. 2 steel, miscellaneous baling and sheet scrap. Average density 50 pounds per cubic foot.

211 Shredded scrap. Homogeneous iron and steel scrap magnetically separated, originating from automobiles, unprepared No. 1 and No. 2 steel, miscellaneous baling and sheet scrap. Average density 70 pounds per cubic foot.

212 Shredded clippings. Shredded 1000 series carbon steel clippings or sheets. Material should have an average density of 60 pounds per cubic foot.

213 Steel can bundles. Steel can scrap compressed to charging box size and weighing not less than 75 pounds per cubic foot. Cans may be baled without removal of paper labels, but free of other non-metallics. May include up to 5 gallon tin coated containers.

214 No. 3 bundles. Old sheet steel, compressed to charging box size and weighing not less than 75 pounds per cubic foot. May include all coated ferrous scrap not suitable for inclusion in No. 2 bundles.

215 Incinerator bundles. Tin can scrap, compressed to charging box size and weighing not less than 75 pounds per cubic foot. Processed through a recognized garbage incinerator.

216 Terne plate bundles. New terne plate sheet scrap, clippings or skeleton scrap, compressed or hand bundled, to charging box size, and weighing not less than 75 pounds per cubic foot. (Hand bundles are tightly secured for handling with a magnet.) May include Stanley balls or mandrel wound bundles or skeleton reels, tightly secured.

217 Bundled No. 1 steel. Wrought iron and/or steel scrap 1/8 inch or over in thickness, compressed to charging box size and weighing not less than 75 pounds per cubic foot. Free of all metal-coated material.

218 Bundled No. 2 steel. Wrought iron or steel scrap, black or galvanized, 1/8 inch and over in thickness, compressed to charging box size and weighing not less than 75 pounds per cubic foot. Auto body and fender stock, burnt or hand stripped, may constitute a maximum of 60 percent by weight. (This percent based on makeup of auto body, chassis, driveshafts, and bumpers.) Free of all coated material, except as found on automobiles.

219 Machine shop turnings. Clean steel or wrought iron turnings, free of iron borings, nonferrous metals in a free state, scale, or excessive oil. May not include badly rusted or corroded stock.

220 Machine shop turnings and iron borings. Same as machine shop turnings but including iron borings.

221 Shoveling turnings. Clean short steel or wrought iron turnings, drillings, or screw cuttings. May include any such material whether resulting from crushing, raking, or other processes. Free of springy, bushy, tangled or matted material, lumps, iron borings, nonferrous metals in a free state, grindings, or excessive oil.

222 Shoveling turnings and iron borings. Same as shoveling turnings, but including iron borings.

223 Iron borings. Clean cast iron or malleable iron borings and drillings, free of steel turnings, scale, lumps or excessive oil.

224 Auto slabs. Clean automobile slabs, cut 3 feet x 18 inches and under.

225 Auto slabs. Clean automobile slabs, cut 2 feet x 18 inches and under.

226 Briquetted iron borings. Analysis and density to consumer’s specifications.

227 Briquetted steel turnings. Analysis and density to consumer’s specifications.

228 Mill scale. Dark colored, ranging from blue to black, ferromagnetic iron oxide forming on the surface of steel articles during heating and working.

Electric Furnace Casting and Foundry Grades

229 Billet, bloom and forge crops. Billet, bloom, axle, slab, heavy plate and heavy forge crops, containing not over 0.05 percent phosphorus or sulphur and not over 0.5 percent silicon, free from alloys. Dimensions not less than 2 inches in thickness, not over 18 inches in width, and not over 36 inches in length.

230 Bar crops and plate scrap. Bar crops, plate scrap, forgings, bits, jars, and tool joints, containing not over 0.05 percent phosphorus or sulphur, not over 0.5 percent silicon, free from alloys. Dimensions not less than 1 /2 inch in thickness, not over 18 inches in width, and not over 36 inches in length.

231 Plate and structural steel, 5 feet and under. Cut structural and plate scrap, 5 feet and under. Clean open hearth steel plates, structural shapes, crop ends, shearings, or broken steel tires. Dimensions not less than 1 /4 inch thickness, not over 5 feet in length and 18 inches in width. Phosphorus or sulphur not over 0.05 percent.

232 Plate and structural steel, 5 feet and under. Cut structural and plate scrap, 5 feet and under. Clean open hearth steel plates, structural shapes, crop ends, shearings, or broken steel tires. Dimensions not less than 1 /4 inch thickness, not over 5 feet in length and 24 inches in width. Phosphorus or sulphur not over 0.05 percent.

233 Cast steel. Steel castings not over 48 inches long or 18 inches wide, and 1 /4 inch and over in thickness, containingnot over 0.05 percent phosphorus or sulphur, free from alloys and attachments. May include heads, gates, and risers.

234 Punchings and plate scrap. Punchings or stampings, plate scrap, and bar crops containing not over 0.05 percent phosphorous or sulphur and not over 0.5 percent silicon, free from alloys. All materials cut 12 inches and under, and with the exception of punchings or stampings, at least 1/8 inch in thickness. Punchings or stampings under 6 inches in diameter may be any gauge.

235 Electric furnace bundles. New black steel sheet scrap hydraulically compressed into bundles of size and weight as specified by consumer.

236 Cut structural and plate scrap, 3 feet and under. Clean open hearth steel plates, structural shapes, crop ends, shearings, or broken steel tires. Dimensions not less than 1/4 inch in thickness, not over 3 feet in length and 18 inches in width. Phosphorus or sulphur not over 0.05 percent.

237 Cut structural and plate scrap, 2 feet and under. Same as cut structural and plate scrap, 3 feet and under, except for length.

238 Cut structural and plate scrap, 1 foot and under. Same as cut structural and plate scrap, 3 feet and under, except for length.

239 Silicon busheling. Clean silicon bearing steel scrap, not exceeding 12 inches in any dimension, including new factory busheling (for example, sheet clippings, stampings, etc.), having a silicon content of 0.05 percent to 5.0 percent.

240 Silicon Clippings. Clean steel scrap, including new factory busheling (for example, sheet clippings, stampings, etc.), may not include old auto body and fender stock. Free of metal coated, limed, vitreous enameled, and electrical sheet containing minimum 1 percent silicon.

241 Chargeable ingots and ingot butts. Chargeable ingots and ingot butts for material to be suitable and acceptable to the consumer containing not over 0.05 percent phosphorus or sulphur and not over 0.05 percent silicon free of alloys.

242 Foundry steel, 2 feet and under. Steel scrap 1/8 inch and over in thickness, not over 2 feet in length or 18 inches in width. Individual pieces free from attachments. May not include nonferrous metals, cast or malleable iron, cable, vitreous enameled, or metal coated material.

243 Foundry steel, 1 foot and under. Same specifications as 2-foot material, except for length.

243A Low residual, black foundry busheling. 1000 series black carbon steel scrap, 1/8 inch and over in thickness, not more than 12 inch x 24 inch, manganese content not more than 0.50 percent. Other parameters subject to agreement between supplier and consumer.

243B Low residual, ductile quality shredded clips. Shredded black 1000 series carbon steel scrap, 1/8 inch and over in thickness, minimum average density of 75 PCF, manganese content not more than 0.50 percent. Other parameters subject to agreement between supplier and consumer.

244 Springs and crankshafts. Clean automotive springs and crankshafts, either new or used.

245 Alloy free turnings. Clean shoveling steel turnings free from lumps, tangled or matted material, iron borings, or excessive oil containing not more than 0.05 percent phosphorus or sulphur, and free of alloys.

246 Alloy free short shoveling steel turnings. Clean shoveling steel turnings, free of lumps, tangled or matted material, iron borings, or excessive oil, containing not more than 0.05 percent phosphorus or sulphur, and free of alloys.

247 Alloy free machine shop turnings. Clean steel turnings, free of iron borings or excessive oil, containing not more than 0.05 percent phosphorus or sulphur, and free of alloys. May not include badly rusted or corroded stock.

248 Hard steel cut 30 inches and under. Automotive steel consisting of rear ends, crankshafts, driveshafts, front axles, springs, and gears prepared 30 inches and under. May not include miscellaneous small shoveling steel or any pieces too bulky for gray iron foundry use.

249 Chargeable slab crops. Chargeable slab crops for material to be suitable and acceptable to the consumer containing not over 0.05 percent phosphorus and 0.05 percent sulphur and not over 0.05 percent silicon and free of alloys.

250 Silicon bundles. Silicon sheet scrap, clippings or skeleton scrap, compressed or hand bundled, to charging box size, and weighing not less than 75 pounds per cubic foot, having a silicon content of 0.50 percent to 5.0 percent.

251 Heavy turnings. Short, heavy steel turnings, containing not over 0.05 percent phosphorus or sulphur and free of alloys. May include rail chips. May not include machine shop or other light turnings and must weigh not less than 75 pounds per cubic foot in the original state of production.

Specially Processed Grades to Meet Consumer Requirements

Cast Iron Grades

252 Cupola cast. Clean cast iron scrap such as columns, pipes, plates, and castings of a miscellaneous nature, including automobile blocks and cast iron parts of agricultural and other machinery. Free from stove plate, burnt iron, brake shoes or foreign material. Cupola size, not over 24 inches x 30 inches, and no piece over 150 pounds in weight.

253 Charging box cast. Clean cast iron scrap in sizes not over 60 inches in length or 30 inches in width, suitable for charging into an open hearth furnace without further preparation. Free from burnt iron, brake shoes, or stove plate.

254 Heavy breakable cast. Cast iron scrap over charging box size or weighing more than 500 pounds. May include cylinders and driving wheel centers. May include steel which does not exceed 10 percent of the casting by weight.

255 Hammer block or bases. Cast iron hammer blocks or bases.

256 Burnt iron. Burnt cast iron scrap, such as stove parts, grate bars, and miscellaneous burnt iron. May include sash weights or window weights.

257 Mixed cast. May include all grades of cast iron except burnt iron. Dimensions not over 24 inches x 30 inches and no piece over 150 pounds in weight.

258 Stove plate, clean cast iron stove. Free from malleable and steel parts, window weights, plow points, or burnt cast iron.

259 Clean auto cast. Clean auto blocks; free of all steel parts except camshafts, valves, valve springs, and studs. Free of nonferrous and non-metallic parts.

260 Unstripped motor blocks. Automobile or truck motors from which steel and nonferrous fittings may or may not have been removed. Free from driveshafts and all parts of frames.

261 Drop broken machinery cast. Clean heavy cast iron machinery scrap that has been broken under a drop. All pieces must be of cupola size, not over 24 inches x 30 inches, and no piece over 150 pounds in weight.

262 Clean auto cast, broken, not degreased. Clean auto blocks, free of all steel parts except camshafts, valves, valve springs and studs. Free of nonferrous and non-metallic parts, and must be broken to cupola size, 150 pounds or less.

263 Clean auto cast, degreased. Free of all steel parts except camshafts, valves, valve springs, and studs. Free of nonferrous and non-metallic parts, and must be broken into cupola size, 150 pounds or less.

264 Malleable. Malleable parts of automobiles, railroad cars, locomotives, or miscellaneous malleable iron castings. Free from cast iron and steel parts and other foreign material.

265 Broken ingot molds and stools. Broken ingot molds and stools, cast iron, maximum size 2 feet x 3 feet x 5 feet.

266 Unbroken ingot molds and stools. Unbroken ingot molds and stools, cast iron. Special Boring Grades

267 No. 1 chemical borings. New clean cast or malleable iron borings and drillings containing not more than 1 percent oil, free from steel turnings, or chips, lumps, scale, corroded or rusty material.

268 Briquetted cast iron borings, hot process. Cast iron borings, heated, briquetted, to a density of approximately 85 percent, oil and water content under 1 percent.

269 Briquetted cast iron borings, cold process. Cast iron boring briquettes, free of steel and nonferrous material, hydraulically compressed into a cohesive solid, reasonably free of oil, and having a density of not less than 60 percent.

270 Malleable borings. Clean malleable iron borings and drillings, free of steel turnings, scale, lumps and excessive oil.

271 No. 2 chemical borings. New clean cast or malleable iron borings and drillings, containing not more than 1.5 percent oil, free from steel turnings, or chips, lumps, scale, corroded or rusty material.

Steel From Scrap Tires General Baled.

Baled—High Density.
Hydraulically compressed, no dimension larger than 24”, density of at least 75 pounds per square foot.

Baled—HRB/Low Density.
Density of less than 75 pounds per square foot. Each bale secured with sufficient number of bale ties drawn tight to insure a satisfactory delivery. Other Means of Preparation. Individual specifications to be agreed upon between consumer and supplier.

272 Pulled bead wire (Truck)—Grade 1. Not chopped; made up of loops of wire. Less than five percent (<5%) rubber/fiber.

273 Pulled bead wire (Truck)—Grade 2. Not chopped; made up of loops of wire. Five to ten percent (5-10%) rubber/fiber.

274 Pulled bead wire (Truck)—Grade 3. Not chopped; made up of loops of wire. Greater than ten percent (>10%) rubber/fiber.

275 Pulled bead wire (Passenger)—Grade 1. Not chopped; made up of loops of wire. Less than five percent (<5%) rubber/fiber.

276 Pulled bead wire (Passenger)—Grade 2. Not chopped; made up of loops of wire. Five to ten percent (5-10%) rubber/fiber.

277 Pulled bead wire (Passenger)—Grade 3. Not chopped; made up of loops of wire. Greater than ten percent (>10%) rubber/fiber.

278 Processed tire wire (Ferrous)—Grade 1. Chopped. Less than two percent (<2%) rubber/fiber.

279 Processed tire wire (Ferrous)—Grade 2. Chopped. Less than five percent (<5%) rubber/fiber.

280 Processed tire wire (Ferrous)—Grade 3. Chopped. Five to ten percent (5-10%) rubber/fiber.

281 Processed tire wire (Ferrous)—Grade 4. Chopped. Ten to twenty percent (10-20%) rubber/ fiber.

282 Processed tire wire (Ferrous)—Grade 5. Chopped. Greater than twenty percent (>20%) rubber/fiber.

Railroad Ferrous Scrap* Specifications of Association of American Railroads promulgated by its Purchases and Materials Management Division (Revised 1973)

(2) Axles, Steel. Solid car and/or locomotive friction bearing, 8 inch diameter and under (free of axles with key-way between wheel seats, no axles of shorter lengths than distance between wheel seats to be included).

(2A) Axles, Steel. Solid car and/or locomotive friction bearing over 8 inch diameter (free of axles with key-way between wheel seats, no axles of shorter length than distance between wheel seats to be included).

(3) Axles, Steel. Roller bearing 8 inch diameter and under (no axles of shorter lengths than distance between wheel seats to be included).

(3A) Axles, Steel. Roller bearing over 8 inch diameter (no axles of shorter length than distance between wheel seats to be included).

(4) Spikes, Track Bolts and Nuts, and Lock Washers, may include Rail Anchors.

(5) Tie Plates. Steel.

(6) Rail Joints, Angle and/or Splice Bars. Steel.

(9) Bolsters and/or Truck Sides, Frames: Uncut. Cast steel.

(11) Cast Steel, No. 2. Steel castings, over 18 inches wide and/or over 5 feet long.

(11A) Cast Steel, No. 1. Steel castings, 18 inches and under, not over 5 feet long, including cut truck side frames and bolsters.

(12) Cast Iron, No. 1. Cast iron scrap, such as columns, pipes, plates, and/ or castings of miscellaneous nature, but free from stove plates, brake shoes, and burnt scrap. Must be cupola size, not over 24 x 30 inches in dimension and no piece to weigh over 150 pounds. Must be free from foreign material.

(13) Cast Iron, No. 2. Pieces weighing over 150 pounds, but not more than 500 pounds. Free from burnt cast.

(14) Cast Iron, No. 3. Pieces weighing over 500 pounds; includes cylinders, driving wheel centers and/or all other castings. (Free from hammer blocks or bases.)

(15) Cast Iron, No. 4. Burnt cast iron scrap, such as grate bars, stove parts and/or miscellaneous burnt scrap.

(16) Cast Iron Brake Shoes. Brakes shoes of all types except composition-filled shoes.

(17) Couplers and/or Knuckles. Railroad car and/or locomotive steel couplers, knuckles and/or locks stripped clean of all other attachments.

(18) Frogs and/or Switches, uncut. Steel frogs and switches that have not been cut apart, exclusive of manganese.

(18A) Railbound Manganese Frogs and Switch Points with manganese inserts that have not been cut apart.

(23) Malleable. Malleable parts of automobiles, railroad cars, locomotive and/or miscellaneous malleable castings.

(24) Melting Steel, Railroad No. 1. Clean wrought iron or steel scrap, 1 /4 inch and over in thickness, not over 18 inches in width, and not over 5 feet in length. May include pipe ends and material 1/8 inch to 1 /4 inch in thickness, not over 15 inches x 15 inches. Individual pieces cut so as to lie reasonably flat in charging box.

(27) Rail, Steel No. 1. Standard section tee rails, original weight 50 pounds per yard or heavier, 10 feet long and over. Suitable for rerolling into bars and shapes. Free from bent and twisted rails, frog, switch, and guard rails, or rails with split heads and broken flanges. Continuous welded rail may be included provided no weld is over 9 inches from the end of the piece of rail.

(28A) Rail, Steel No. 2 Cropped Rail Ends. Standard section, original weight of 50 pounds per yard and over, 18 inches long and under.

(28B) Rail, Steel No. 2 Cropped Rail Ends. Standard section, original weight of 50 pounds per yard and over, 2 feet long and under.

(28C) Rail, Steel No. 2 Cropped Rail Ends. Standard section, original weight 50 pounds per yard and over, 3 feet long and under.

(29) Rail, Steel No. 3. Standard section tee, girder, and/or guard rails, to be free from frog and switch rails not cut apart, and contain no manganese, cast, welds, or attachments of any kind except angle bars. Free from concrete, dirt, and foreign material of any kind.

(30) Sheet Scrap, No. 1. Under 3/16 inch thick, may include hoops, band iron and/or steel, scoops and/or shovels (free of wood). Must be free from burnt or metal coated material, cushion, or other similar springs.

(31) Sheet Scrap, No. 2. Galvanized or tinned material and/or gas retorts, and/or any other iron or steel material not otherwise classified.

(32) Steel, Tool. (Specify kind in offering.)

(33) Steel, Manganese. All kinds of manganese, rail, guard rails, frogs and/or switch points, cut or uncut.

(34) Steel, Spring. Coil and/or elliptical, minimum thickness 1 /4 inch, may be assembled or cut apart.

(34A) Steel, Spring. Coil only.

(35) Structural, Wrought Iron and/or Steel Uncut. All steel or steel mixed with iron from bridges, structures and/or equipment that has not been cut apart, may include uncut bolsters, brakebeams, steel trucks, underframes, channel bars, steel bridge plates, frog and/or crossing plates and/or other steel of similar character.

(36) Tires. All locomotive, not cut to specified lengths.

(38) Turnings. No. 1. Heavy turnings from wrought iron and/or steel railroad axles or heavy forgings and/or rail chips, to weigh not less than 75 pounds per cubic foot. Free from dirt or other foreign material of any kind. Alloy steel scrap may be excluded from these specifications by mutual agreement between buyer and seller.

(38A) Turnings, Drillings and/or Borings. No. 2. Cast, wrought, steel and/or malleable iron borings, turnings and/or drillings mixed with other metals.

(40) Wheels, No. 1. Cast iron car wheels.

(42) Wheels, No. 3. Solid cast steel, forged, pressed and/or rolled steel car and/or locomotive wheels, not over 42 inches diameter. (Specify kind in offering.)

(45) Destroyed Steel Cars. Bodies of steel cars cut apart sufficiently to load. (Specify kind.)

(45A) Destroyed Steel Car Sides and Box Car Roofs. Cut to a maximum length of… and a maximum width of… suitable for use in super presses and shears without additional preparation.